Calcium hexaboride (sometimes calcium boride) is a compound of calcium and boron with the chemical formula CaB<sub>6</sub>. It is an important material due to its high electrical conductivity , hardness, chemical stability, and melting point. It is a black, lustrous, chemically inert powder with a low density. It has the cubic structure typical for metal hexaborides, with octahedral units of 6 boron atoms combined with calcium atoms. CaB<sub>6</sub> and lanthanum-doped CaB<sub>6</sub> both show weak ferromagnetic properties, which is a remarkable fact because calcium and boron are neither magnetic, nor have inner 3d or 4f electronic shells, which are usually required for ferromagnetism.
CaB<sub>6</sub> has been investigated in the past due to a variety of peculiar physical properties, such as superconductivity, valence fluctuation and Kondo effects. However, the most remarkable property of CaB<sub>6</sub> is its ferromagnetism. It occurs at unexpectedly high temperature (600 K) and with low magnetic moment (below 0.07 per atom). The origin of this high temperature ferromagnetism is the ferromagnetic phase of a dilute electron gas, linkage to the presumed excitonic state in calcium boride, or external impurities on the surface of the sample. The impurities might include iron and nickel, probably coming from impurities in the boron used to prepare the sample.
CaB<sub>6</sub> is insoluble in H<sub>2</sub>O, MeOH (methanol), and EtOH (ethanol) and dissolves slowly in acids. Its microhardness is 27 GPa, Knoop hardness is 2600 kg/mm<sup>2</sup>), Young modulus is 379 GPa, and electrical resistivity is greater than 2÷10<sup>10</sup> é÷m for pure crystals. CaB<sub>6</sub> is a semiconductor with an energy gap estimated as 1.0 eV. The low, semi-metallic conductivity of many CaB<sub>6</sub> samples can be explained by unintentional doping due to impurities and possible non-stoichiometry.
The crystal structure of calcium hexaboride is a cubic lattice with calcium at the cell centre and compact, regular octahedra of boron atoms linked at the vertices by B-B bonds to give a three-dimensional boron network. Each calcium has 24 nearest-neighbor boron atoms The calcium atoms are arranged in simple cubic packing so that there are holes between groups of eight calcium atoms situated at the vertices of a cube. The simple cubic structure is expanded by the introduction of the octahedral B<sub>6</sub> groups and the structure is a CsCl-like packing of the calcium and hexaboride groups. Another way of describing calcium hexaboride is as having a metal and a B<sub>6</sub><sup>2âÂÂ</sup> octahedral polymeric anions in a CsCl-type structure where the Calcium atoms occupy the Cs sites and the B<sub>6</sub> octahedra in the Cl sites. The Ca-B bond length is 3.05 àand the B-B bond length is 1.7 à.
<sup>43</sup>Ca NMR data contains ô<sub>peak</sub> at âÂÂ56.0 ppm and ô<sub>iso</sub> at âÂÂ41.3 ppm where ô<sub>iso</sub> is taken as peak max +0.85 width, the negative shift is due to the high coordination number.
Raman Data: Calcium hexaboride has three Raman peaks at 754.3, 1121.8, and 1246.9 cm<sup>âÂÂ1</sup> due to the active modes A<sub>1g</sub>, E<sub>g</sub>, and T<sub>2g</sub> respectively.
Observed Vibrational Frequencies cm<sup>âÂÂ1</sup> : 1270(strong) from A<sub>1g</sub> stretch, 1154 (med.) and 1125(shoulder) from E<sub>g</sub> stretch, 526, 520, 485, and 470 from F<sub>1g</sub> rotation, 775 (strong) and 762 (shoulder) from F<sub>2g</sub> bend, 1125 (strong) and 1095 (weak) from F<sub>1u</sub> bend, 330 and 250 from F<sub>1u</sub> translation, and 880 (med.) and 779 from F<sub>2u</sub> bend.
Other methods of producing CaB<sub>6</sub> powder include:
results in relatively poor quality material.
Calcium hexaboride is used in the manufacturing of boron-alloyed steel and as a deoxidation agent in production of oxygen-free copper. The latter results in higher conductivity than conventionally phosphorus-deoxidized copper owing to the low solubility of boron in copper. CaB<sub>6</sub> can also serve as a high temperature material, surface protection, abrasives, tools, and wear resistant material.
CaB<sub>6</sub> is highly conductive, has low work function, and thus can be used as a hot cathode material. When used at elevated temperature, calcium hexaboride will oxidize degrading its properties and shortening its usable lifespan.
CaB<sub>6</sub> is also a promising candidate for n-type thermoelectric materials, because its power factor is larger than or comparable to that of common thermoelectric materials Bi<sub>2</sub>Te<sub>3</sub> and PbTe.
CaB also can be used as an antioxidant in carbon bonded refractories.